Rare earth nitrides and their applications in magnetic tunnel junctions

Download (73.52 MB)
thesis
posted on 2021-12-07, 19:47 authored by Ullstad, Felicia

In this thesis, we investigate the rare earth nitrides, a family of materials containing many intrinsic ferromagnetic semiconductors, with a particular focus on GdN and SmN.We investigate the rare earth nitride formation reaction, explore some properties of GdN and SmN, and finally manufacture and measure magnetic tunnel junctions which incorporate rare earth nitrides. The investigations of the reaction and properties of the materials are used to improve and understand the magnetic tunnel junctions. All samples and devices are grown at room temperature, giving polycrystalline rare earth nitride films.  We show that a rare earth surface can catalytically break theN2 molecule at ambient temperature and low pressures. We follow the nitrogen reacting with the rare earth to form a rare earth nitride in real time via conductance measurements. By comparing the N2 cracking, reaction, and diffusion at both a RE and a REN surface we propose a pressure range in which the nitrogen content in SmN can be manipulated and conclude that the nitrogen in the top monolayers in a SmN film is mobile.  In the investigation of GdN and SmN, we find that the conductivity of SmN follows the same behaviour as GdN when changing the N2 pressure during deposition. We follow the conductance change in SmN during deposition and propose a minimum thickness for room temperature deposited SmN films for consistent conductivity measurements. We report structural and magnetic changes in GdN which has been exposed to N-ions. We also present data on materials making ohmic contact to both GdN and SmN.  Finally, we report the manufacturing and investigation of magnetic tunnel junctions using GdN and SmN electrodes with a GaN tunnel barrier. A new pattern design produces 20 devices, in a single deposition, which show consistent behaviour and expands on previous work on this topic. The main focus of the investigation is the J-V characteristics of the magnetic tunnel junctions which shows clear non-linear behaviour arising from tunnelling through the GaN. A Simmons fit to the J-V characteristics yields a barrier height of 0:8 eV and barrier thicknesses close to experimentally determined thicknesses. The J-V characteristics are investigated with changing temperature and changing applied magnetic field to investigate the effect of the ferromagnetism of the GdN and SmN electrodes. The tunnel magnetoresistance (TMR) of the devices show two contributions, a low-temperature TMR contribution and a 50K TMR contribution, and the maximum TMR for all devices are between 100% to 600%. The devices can withstand current densities up to 4000A/cm² and voltages up to 5V which is promising for a wide range of future applications.

History

Copyright Date

2019-01-01

Date of Award

2019-01-01

Publisher

Te Herenga Waka—Victoria University of Wellington

Rights License

Author Retains Copyright

Degree Discipline

Physics

Degree Grantor

Te Herenga Waka—Victoria University of Wellington

Degree Level

Doctoral

Degree Name

Doctor of Philosophy

Victoria University of Wellington Unit

Macdiarmid Institute for Advanced Materials and Nanotechnology

ANZSRC Type Of Activity code

1 PURE BASIC RESEARCH

Victoria University of Wellington Item Type

Awarded Doctoral Thesis

Language

en_NZ

Victoria University of Wellington School

School of Chemical and Physical Sciences

Advisors

Trodahl, Joe; Ruck, Ben